钢筋混凝土钢种的调整!

添加时间:2018-12-07      发布人:http://www.jzqgc.com

  调整了钢筋混凝土用钢种
  Steel grades for reinforced concrete have been adjusted
  (1)列入500MPa钢筋。考虑到500MPa级钢筋应用的实际需求,在进行大量试验研究和试点工程应用的基础上,在《设计规范》中列入了500MPa级500MPa并对其设计计算、配筋构造均提出了细致要求。但考虑到缺少相应的试验数据,500MPa钢筋的疲劳设计参数仍未列入。
  (1) Include 500 MPa steel bar. Considering the actual demand of 500 MPa grade steel bar application, on the basis of a large number of experimental research and pilot project application, 500 MPa grade 500 MPa is included in the Design Code for the first time, and detailed requirements are put forward for its design calculation and reinforcement structure. However, considering the lack of relevant test data, the fatigue design parameters of 500 MPa steel bars have not been included.
  (2)列入细晶粒钢筋。以前期材料及结构研究为基础,纳入了HRBF335. HRBF400、HRBF500三种细晶粒钢筋。但考虑到细晶粒钢筋焊接的实际问题,《设计规范》提出细晶粒钢筋的焊接应经试验确定。
  (2) Include fine grain reinforced bar. On the basis of previous material and structure studies, three kinds of fine grain reinforced bars, HRBF335. HRBF400 and HRBF500, were included. However, considering the actual problem of welding fine grain steel bar, the Code of Design proposes that the welding of fine grain steel bar should be determined by test.
  (3)以HPB300钢筋替代HPB235钢筋。根据标准《钢筋混凝土用钢 第1部分:热轧光圆钢筋》( GB 1499. 1-2008)的规定,考虑到推广高强钢筋的需要,建筑工程中淘汰HPB235光圆钢筋,推广应用HPB300钢筋。
济南钢筋批发
  (3) Replace HPB235 steel bar with HPB300 steel bar. According to the national standard "Steel for Reinforced Concrete Part 1: Hot Rolled Round Reinforcement Bar" (GB 1499.1-2008), considering the need to promote high-strength reinforcement, HPB235 round reinforcement bars were eliminated in construction projects, and HPB300 reinforcing bars were comprehensively promoted and applied.
  (4)保留了RRB400钢筋。《设计规范》保留了RRB400钢筋品种,但规定不宜焊接。可理解为此钢筋即为新修订的《钢筋混凝土用余热处理钢筋》( GB 13014-1991)中的不可焊余热处理钢筋RRB400,RRB400W钢筋虽未列入,但如有可靠焊接依据,也可应用。HRB500钢筋由于(GB 13014-1991)产品标准修订未及时完成,暂未纳入。
  (4) RRB400 reinforcing bar was retained. The RRB400 steel bar is retained in the Design Code, but it is not suitable for welding. It can be understood that the reinforcing steel bar is RRB400, which is a non-weldable waste heat treatment reinforcing steel bar in the newly revised GB 13014-1991. Although RRB400W reinforcing steel bar is not included, it can also be applied if there is reliable welding basis. HRB500 reinforcing bar has not been included in the revised product standard (GB 13014-1991).
  注:1.用作受剪、受扭、受冲切承载力计算的箍筋,抗拉设计强度fyv按fy数值取用,但其数值小应大于360N/mm2:
  Note: 1. For stirrups used for calculating shear, torsion and punching shear capacity, the tensile design strength FYV is chosen according to the value of fy, but its value should be smaller than 360N/mm2:
  2.用作局部承压的间接配筋,以及受压构件约束混凝上配置的箍筋,抗拉设计强度fy按表中数值取用。
  2. As indirect reinforcement for local compression and stirrups for confined coagulation of compressive members, the tensile design strength FY is selected according to the values in the table.
  以上内容由济南钢筋批发整理发布,更多相关内容可以点击咨询:http://www.jzqgc.com/
  The above contents are wholesaled and published by Jinan reinforcing steel bar. More related contents can be clicked for consultation: http://www.jzqgc.com/